Films were deposited from aluminum acetylacetonate (Al(acac)3) using a methodology involving reactive sputtering and low energy ion bombardment. The plasma was generated by the application of radiofrequency power to the powder containing electrode and simultaneously, negative pulses were supplied to the electrode where the substrates were attached. It was investigated the effect of the duty cycle of the pulses (Δ) on the properties of the coatings. Association of ion bombardment to the deposition process increased film thickness, structure reticulation and organic content. Ions from the deposition environment were implanted at the film-air interface or underneath it. Morphology and topography were altered depending on Δ. Considering the enhancement of Δ, it affected the flux of ions reaching the depositing interface and then the deposition rate, H content, crosslinking degree and surface microstructure. Alumina groups were detected in the infrared spectra, whereas the precipitation of amorphous alumina was confirmed by X-ray diffraction.

Alumina films were deposited from a new plasma method using aluminum acetylacetonate (AAA) powder as precursor. The AAA was sputtered in argon and oxygen plasma mixtures. It was investigated the effect of the oxygen proportion (O2%) on the properties of the coatings. Deposition rate was derived from the layer height measured by profilometry. The elemental composition and molecular structure of the films were determined by Rutherford backscattering and infrared spectroscopies, respectively. Grazing incidence X-ray diffraction was used to investigate the microstructure of the films while hardness was determined by nanoindentation technique. Inspections on the surface morphology and on the film composition were conducted associating scanning electron microscopy and energy dispersive spectroscopy. Incorporation of oxygen affects the plasma kinetics and consequently the properties of the coatings. As moderated concentrations of oxygen (< 25%) are added, the structure is predominantly organic containing stoichiometric amorphous alumina. On the other hand, as high O2% (> 25%) are incorporated, the structure become rich in metallic aluminum with carbon rising at low proportions. The deposited layer is not homogeneous in thickness once the chemical composition of the precursor is changed by the action of the reactive oxygen plasma. Oxygen ablation on the film surface also contributes to the lack of homogeneity of the structure, especially as high oxygen proportions are imposed. Hardness data (0.5-2.0 GPa) corroborated the idea of an amorphous structure. Based on the results presented here it was possible to identify the oxygen concentration in the plasma atmosphere which mostly removed organics while preserving the stoichiometric alumina precipitation, subject of great relevance as one considers the reduction in the energy necessary for the creation of fully oxide coatings.

This paper describes the application of two techniques, ANAA and PIXE, used in the analyses of some available commercial food containing regular and genetically modified ingredients, as well as soybens cultivated with regular and genetically modified seeds (GMS). The aim of this work is determine their elemental composition to perform a comparative analysis. The elemental composition results of both types of food, obtained by the two techniques, were in agreement for all elements. Our results show the same elemental composition for all food samples but the quantitative analysis between soybeans seeds (regular and GM) suggested that the product made with GMS have higher concentration values, mainly for Cl, P and Zn, while for industrialized food, made with genetically modified products, a low concentration values were measured for most of the elements.

O presente trabalho foi realizado utilizando a cebola comum (Allium cepa L.) como bioindicador da toxicidade de metais pesados em água de rio. As águas de teste foram coletadas em dois locais: na nascente e na foz do rio Toledo. Os bulbos de A. cepa L. foram cultivados em água de teste com nove níveis de concentração de cobre, zinco e chumbo de 0,1 a 50 ppm. Em laboratório a influência destes líquidos de teste em crescimento de raiz foi examinada durante cinco dias. Em todos os líquidos de teste o metal dissolvido contido foi medido pela técnica TXRF. Para líquidos de teste contendo 0,1-ppm de Cu dissolvido o crescimento da raiz foi reduzido em 50%. Entretanto, ocorreu a mesma redução para 1-ppm de Zn dissolvido. Para Pb dissolvido, o método do Allium teste revela toxidade acima de 0,1 e 0,5 ppm para a nascente e a foz do rio Toledo, respectivamente.

The present work was performed using the common onion (Allium cepa L.) as a bioindicator of toxicity of heavy metals in river water. The test waters were collected at two sampling sites: at the beginning and the end of the Toledo River. The bulbs of A. cepa L. were grown in test water with nine concentration levels of copper, zinc and lead from 0.1 to 50 ppm. In the laboratory, the influence of these test liquids on the root growth was examined during five days. For test liquids containing below 0.03-ppm dissolved Cu the root growth was reduced by 40% However, the same reduction occurred for 1-ppm dissolved Zn. For dissolved Pb, results reveal toxicity above 0.1 and 0.6 ppm at the beginning and the end of the Toledo river water, respectively.